RESUMO
OBJECTIVES: Previous efforts led to the development of two different polymeric biomaterials for periodontal regeneration with antibacterial photodynamic surface activity. The present study aimed to investigate osseointegration and bone formation of both materials in an ovine model. METHODS: Both biomaterials: 1) urethane dimethacrylate-based Biomaterial 1 (BioM1) and 2) tri-armed oligoester-urethane methacrylate-based Biomaterial 2 (BioM2) are enriched with beta-tri-calcium phosphate and the photosensitizer meso-tetra(hydroxyphenyl)chlorin (mTHPC). These materials were implanted in non-critical size bone defects in the sheep femur (n = 16) and tibia (n = 8). Empty defects served as controls (n = 16). Polyfluorochrome sequential bone labeling was carried out at baseline and after 3, 6, and 12 months. Animals were sacrificed after 12 months. Bone specimens (n = 40) were fixed and subjected to microtomographic analysis (µCT) for the evaluation of the bone-volume-fraction (BV/TV), trabecular number and trabecular thickness. Subsequently, histological sections were arranged and polyfluorochrome sequential bone labeling was analyzed by confocal laser scanning microscopy (cLSM). RESULTS: cLSM analysis revealed that highest remodeling and bone formation activity occurred during the second half of the study period (6-12 months). Bone formation in the tibia was significantly lower for the control (2.71 ± 1.26%) as compared to BioM1 (6.01 ± 2.99%) and BioM2 (6.45 ± 2.12%); (p = 0.006, p = 0004). Micro-computed tomography revealed a BV/TV volume fraction of 44.72 ± 9.01% in femur defects filled with BioM1 which was significantly higher compared to the control (32.27 ± 7.02%; p = 0.01). Bone architecture (trabecular number, trabecular thickness) did not significantly differ from the self-healed defects. SIGNIFICANCE: Both biomaterials, especially BioM1 showed good osseointegration and bone formation characteristics and can be recommended for further examination in periodontal regeneration studies.
RESUMO
OBJECTIVE: Biomaterials for periodontal regeneration may have insufficient mechanical and antimicrobial properties or are difficult to apply under clinical conditions. The aim of the present study was to develop a polymeric bone grafting material of suitable physical appearance and antimicrobial photodynamic activity. METHODS: Two light curable biomaterials based on urethane dimethacrylate (BioM1) and a tri-armed oligoester-urethane methacrylate (BioM2) that additionally contained a mixture of ß-tricalcium phosphate microparticles and 20wt% photosensitizer mTHPC (PS) were fabricated and analyzed by their compressive strength, flexural strength and modulus of elasticity. Cytotoxicity was observed by incubating eluates and in direct-contact to MC3T3-E1 cells. Antimicrobial activity was ascertained on Porphyromonas gingivalis and Enterococcus faecalis upon illumination with laser light (652nm, 1×100J/cm2, 2×100J/cm2). RESULTS: The compressive strength, flexural strength and elastic modulus were, respectively, 311.73MPa, 22.81MPa and 318.85MPa for BioM1+PS and 742.37MPa, 7.58MPa and 406.23MPa for BioM2+PS. Both materials did not show any cytotoxic behavior. Single laser-illumination (652nm) caused total suppression of P. gingivalis (BioM2+PS), while repeated irradiation reduced E. faecalis by 3.7 (BioM1+PS) and 3.1 (BioM2+PS) log-counts. SIGNIFICANCE: Both materials show excellent mechanical and cytocompatible properties. In addition, irradiation with 652nm induced significant bacterial suppression. The manufactured biomaterials might enable a more efficient cure of periodontal bone lesions. Due to the mechanical properties functional stability might be increased. Further, the materials are antimicrobial upon illumination with light that enables a trans-mucosal eradication of residual pathogens.
